T.I. Korányi et al. / Journal of Catalysis 253 (2008) 119–131
131
the SBA-15 than on the traditional silica-supported nickel phos-
phide catalysts.
References
[1] S.T. Oyama, J. Catal. 216 (2003) 343.
5
. Conclusion
[2] R. Iwamoto, J. Grimblot, Adv. Catal. 44 (2000) 417.
[
3] R. Prins, V.H.J. de Beer, G.A. Somorjai, Catal. Rev.-Sci. Eng. 31 (1989) 1.
4] S. Eijsbouts, Ph.D. thesis, Eindhoven University of Technology, Eind-
hoven, 1989.
[
We prepared three different Ni12P5- and Ni2P-containing
catalysts supported on ordered SBA-15 mesoporous silica by
reduction starting from impregnated nickel phosphate precur-
sors with initial P/Ni molar ratios of 0.5, 0.8, and 2. This varied
phosphorus content produced a significant effect on both the
structure and activity of the catalysts. Using a stoichiometric
phosphorus amount, we obtained Ni12P5 with a relatively ho-
mogeneous particle size distribution. For this SBAS catalyst,
active site densities, derived from CO chemisorption and from
the nickel phosphide particle size, were in good agreement. On
the other hand, when a high excess of phosphorus was used in
the preparation (SBAH) so as to arrive at Ni2P active phases,
CO chemisorption was impeded. Further characterization in-
dicated that the lower accessibility of the Ni2P particles was
caused by pore blocking with phosphate species. A slight ex-
cess of phosphorus (SBAE) also blocked the pores and yielded
a mixture of Ni2P and Ni12P5 in the SBA-15 catalyst. Thus, in
the absence of excess phosphate species that block the meso-
pores, high dispersion of Ni12P5 was observed in SBA-15. The
presence of phosphate species resulted in lower CO chemisorp-
tion because part of the active phase was not formed (due to
partial reduction or reoxidation after passivation), another part
was not accessible (due to pore-plugging), and only a small part
of nickel was in an accessible Ni2P form. Whereas the activity
per unit catalyst mass was highest in the Ni12P5-containing cat-
alyst, the intrinsic activities per unit accessible sites show that
Ni2P was more active. The SBA-15-supported Ni12P5 catalysts
indicated similar activity (turnover rate) to Ni2P/SiO2 whilst the
SBA-15-supported Ni2P phase outperformed Ni2P/SiO2. In-
deed, for ordered mesoporous silica-supported Ni2P, the excess
of phosphate species limited metal utilization in hydrotreating
reactions.
[
5] W.R.A.M. Robinson, T.I. Korányi, A.M. van der Kraan, V.H.J. de Beer,
Final Report, E.C. Contract JOUF-0049-C, 1994.
[6] T.I. Korányi, Appl. Catal. A 239 (2003) 253.
[7] W.R.A.M. Robinson, J.N.M. van Gestel, T.I. Korányi, S. Eijsbouts, A.M.
van der Kraan, J.A.R. van Veen, V.H.J. de Beer, J. Catal. 161 (1996)
539.
[8] C. Stinner, R. Prins, Th. Weber, J. Catal. 202 (2001) 187.
[9] V. Zuzaniuk, C. Stinner, R. Prins, Th. Weber, Stud. Surf. Sci. Catal. 143
(
2002) 247.
10] C. Stinner, Z. Tang, M. Haouas, Th. Weber, R. Prins, J. Catal. 208 (2002)
56.
[11] V. Zuzaniuk, R. Prins, J. Catal. 219 (2003) 85.
[12] S.T. Oyama, X. Wang, Y.-K. Lee, W.-J. Chun, J. Catal. 221 (2004)
[
4
263.
[
[
13] S.J. Sawhill, D.C. Phillips, M.E. Bussell, J. Catal. 215 (2003) 208.
14] S.T. Oyama, X. Wang, Y.-K. Lee, K. Bando, F. Requejo, J. Catal. 210
(2002) 207.
[
15] S.J. Sawhill, K.A. Layman, D.R. van Wyk, M.H. Engelhard, C. Wang,
M.E. Bussell, J. Catal. 231 (2005) 300.
[16] P. Clark, S.T. Oyama, J. Catal. 218 (2003) 78.
[17] Y. Shu, S.T. Oyama, Carbon 43 (2005) 1517.
18] Y. Shu, S.T. Oyama, Chem. Commun. (2005) 1143.
[
[
19] A. Wang, L. Ruan, Y. Teng, X. Li, M. Lu, J. Ren, Y. Wang, Y. Hu, J. Catal.
229 (2005) 314.
[
[
20] Y.-K. Lee, Y. Shu, S.T. Oyama, Appl. Catal. A 322 (2007) 191.
21] R. Nava, J. Morales, G. Alonso, C. Ornelas, B. Pawelec, J.L.G. Fierro,
Appl. Catal. A 321 (2007) 58.
[22] M. Choi, W. Heo, F. Kleitz, R. Ryoo, Chem. Commun. (2003) 1340.
[23] T.I. Korányi, Z. Vít, J.B. Nagy, Catal. Today 130 (2008) 80.
[24] Z. Vít, J. Cinibulk, D. Gulková, Appl. Catal. A 272 (2004) 99.
[
[
[
[
[
[
25] Z. Vít, M. Zdražil, J. Catal. 119 (1989) 1.
26] X. Wang, P. Clark, S.T. Oyama, J. Catal. 208 (2002) 321.
27] X. Liu, J. Chen, J. Zhang, Catal. Commun. 8 (2007) 1905.
28] A. Tuel, L. Canesson, J.C. Volta, Colloids Surf. A 158 (1999) 97.
29] K. Eichele, R.E. Wasylishen, J. Phys. Chem. 98 (1994) 3108.
30] G.C. Gunter, R. Craciun, M.S. Tam, J.E. Jackson, D.J. Miller, J. Catal. 164
Acknowledgments
(1996) 207.
[
[
31] T.R. Krawietz, P. Lin, K.E. Lotterhos, P.D. Torres, D.H. Barich, A. Clear-
field, J.F. Haw, J. Am. Chem. Soc. 120 (1998) 8502.
32] A.H. Janssen, P. van der Voort, A.J. Koster, K.P. de Jong, Chem. Commun.
The authors thank Dr. I. Sajó for providing the XRD pat-
terns, Dr. M. Hegedus for the providing CO adsorption data
from the Chemical Research Center (Hungary), Professor
J.W. Niemantsverdriet (Eindhoven University of Technology)
for providing the XPS measurements, Adelheid Elemans-
Mehring and Tiny Verhoeven (Eindhoven University) for pro-
viding the ICP-OES and XPS measurements, and Dr. K. Polyak
(2002) 1632.
[
[
33] S. Yang, C. Liang, R. Prins, J. Catal. 237 (2006) 118.
34] D. Briggs, M.P. Seah (Eds.), Practical Surface Analysis by Auger and
X-Ray Photoelectron Spectroscopy, Wiley, New York, 1983.
35] J.A. Rodriguez, J.-Y. Kim, J.C. Hanson, S.J. Sawhill, M.E. Bussell,
J. Phys. Chem. B 107 (2003) 6276.
[
(
Pannon University) for determining the elemental composition
of the samples. The authors are indebted to Professor J.B. Nagy
FUNDP, Namur, Belgium) for the use of the NMR and TEM
[36] A.E. Nelson, M. Sun, A.S.M. Junaid, J. Catal. 241 (2006) 180.
[
[
[
37] F. Sun, W. Wu, Z. Wu, J. Guo, Z. Wei, Y. Yang, Z. Jiang, F. Tian, C. Li,
J. Catal. 228 (2004) 298.
(
38] A. Wang, L. Ruan, Y. Teng, X. Li, M. Lu, J. Ren, Y. Wang, Y. Hu, J. Catal.
facilities. Financial support was provided by the FNRS (Bel-
gium), the GACR (Czech Republic; grant 104/06/0870), the
National Creative Research Initiative Program, and the Brain
Korea 21 Program.
229 (2005) 314.
39] M. Houalla, N.K. Nag, A.V. Sapre, D.H. Broderick, B.C. Gates, AIChE
J. 24 (1978) 1015.
[40] M. Egorova, R. Prins, J. Catal. 221 (2004) 11.