Carbohydrate Polymers p. 1017 - 1026 (2016)
Update date:2022-08-17
Topics:
Cui, Ning
Qian, Junmin
Xu, Weijun
Xu, Minghui
Zhao, Na
Liu, Ting
Wang, Hongjie
In the present study, poly(Nε-acryloyl-l-lysine)/hyaluronic acid (pLysAAm/HA) interpenetrating network (IPN) hydrogels were successfully fabricated through the combination of hydrazone bond crosslinking and photo-crosslinking reactions. The HA hydrogel network was first synthesized from 3,3′-dithiodipropionate hydrazide-modified HA and polyethylene glycol dilevulinate by hydrazone bond crosslinking. The pLysAAm hydrogel network was prepared from Nε-acryloyl-l-lysine and N,N′-bis(acryloyl)-(l)-cystine by photo-crosslinking. The resultant pLysAAm/HA hydrogels had a good shape recovery property after loading and unloading for 1.5 cycles (up to 90%) and displayed a highly porous microstructure. Their compressive moduli were at least 5 times higher than that of HA hydrogels. The pLysAAm/HA hydrogels had an equilibrium swelling ratio of up to 37.9 and displayed a glutathione-responsive degradation behavior. The results from in vitro biocompatibility evaluation with pre-osteoblasts MC3T3-E1 cells revealed that the pLysAAm/HA hydrogels could support cell viability and proliferation. Hematoxylin and eosin staining indicated that the pLysAAm/HA hydrogels allowed cell and tissue infiltration, confirming their good in vivo biocompatibility. Therefore, the novel pLysAAm/HA IPN hydrogels have great potential for bone tissue engineering applications.
View MoreHANGZHOU ZHONGCHANG SCIENTIFIC CO.,LTD
Contact:+86-571-88932183
Address:Hangzhou
Beijing Mediking Biopharm Co., Ltd.
Contact:+86-10-89753524/81760121/81769521
Address:Hongxianghong Incubator, Beiqijia Town, Changping district, Beijing, China
Contact:86-15588110016
Address:LINYI CITY,SHANDONG PROVINCE,CHINA
Zhejiang Newfine Industry Co.,Ltd.
Contact:+86-573-82262042
Address:No.225,Dongqing Road, garoms@163.com
Jiangsu Willing Bio-Tech Co ltd
website:http://www.willingbio.com/
Contact:+86 18796909136
Address:No 18 Guoqiao Road
Doi:10.1016/j.tet.2018.09.040
(2018)Doi:10.1021/ja02244a003
(1918)Doi:10.1016/j.saa.2011.12.043
(2012)Doi:10.1039/c4cy00387j
(2014)Doi:10.1039/c6ta06442f
(2017)Doi:10.1248/cpb.28.1071
(1980)