A new approach for preparation of semi-transparent superhydrophobic coatings by ultrasonic spray hydrolysis of Methyltrimethoxysilane (cas 1185-55-3)
-
Add time:07/15/2019 Source:sciencedirect.com
A novel nebulizing spray hydrolysis approach was used for preparation of semi-transparent superhydrophobic coatings. Methyltrimethoxysilane was dissolved in water:ethanol mixture and ultrasonically sprayed on different substrates. Superhydrophobic coatings with a contact angle (CA) as high as 164° and a sliding angle below 5° were obtained. FESEM and AFM revealed a hierarchical micro-nano binary structure with nanometric roughness of the coatings. The coated glass substrate exhibited transmittance close to 80%. The prepared coating showed great self-cleaning and water jet repellency behaviors. The superhydrophobicity of the samples was remained after subjecting to ambient conditions for 50 days. The coating was also durable under water flushing test.
We also recommend Trading Suppliers and Manufacturers of Methyltrimethoxysilane (cas 1185-55-3). Pls Click Website Link as below: cas 1185-55-3 suppliers
Prev:Biological effectiveness of archaeological oak wood treated with Methyltrimethoxysilane (cas 1185-55-3) and PEG against Brown-rot fungi and moulds
Next:Excess molar volume along with refractive index for binary systems of dimethoxymethylphenylsilane with Dimethyldimethoxysilane (cas 1112-39-6), dimethyldiethoxylsilane, methylvinyldiethoxysilane and ethenyltrimethoxysilane) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Biological effectiveness of archaeological oak wood treated with Methyltrimethoxysilane (cas 1185-55-3) and PEG against Brown-rot fungi and moulds07/14/2019
- Application of Methyltrimethoxysilane (cas 1185-55-3) to increase dimensional stability of waterlogged wood07/13/2019
- Methyltrimethoxysilane (cas 1185-55-3) as a stabilising agent for archaeological waterlogged wood differing in the degree of degradation07/12/2019
- Effect of surface modification of CaCO3 nanoparticles by a silane coupling agent Methyltrimethoxysilane (cas 1185-55-3) on the stability of foam and emulsion07/11/2019