Hydrothermal improvement for 3R-CuFeO2 delafossite (cas 12013-12-6) growth by control of mineralizer and reaction atmosphere
-
Add time:08/02/2019 Source:sciencedirect.com
delafossite (cas 12013-12-6) CuFeO2 oxides were grown inside a hydrothermal reactor using Cu2O and FeOOH as precursors and NaOH as mineralizer. During this work the effect of the NaOH mineralizer and the reaction atmosphere was studied by varying the amount of NaOH used in the hydrothermal synthesis and by changing the reactor atmosphere from room air to high purity nitrogen. The oxides obtained were analyzed with Raman Spectroscopy, Fourier Transform Infrared Spectroscopy (FT-IR), X-ray diffraction (XRD), X-ray Photoelectron spectroscopy (XPS), Field Emission Scanning Electron Microscopy (FESEM) and Energy Dispersive X-ray Spectroscopy (EDS), in order to obtain their morphological, chemical and structural characteristics. It was found that increasing the amount of mineralizer from 0.4 g up to 1.02 g improves considerably the hydrothermal reaction efficiency obtaining a resulting oxide with 93% of 3R-CuFeO2 phase and a subsequent decrease of the 2H-CuFeO2 phase. Moreover, using the same hydrothermal route it was shown possible to obtain high purity CuFeO2 compounds using small amounts of NaOH (0.4 g) if the reaction is performed under a non-oxidative atmosphere injecting pure nitrogen gas to the hydrothermal reactor where an increase of 3R-CuFeO2 phase from 36% to 94% was obtained. Finally, direct band gap of the semiconducting oxides were estimated using Tauc method from UV–vis spectra obtained by Diffuse Reflectance spectroscopy.
We also recommend Trading Suppliers and Manufacturers of delafossite (cas 12013-12-6). Pls Click Website Link as below: cas 12013-12-6 suppliers
Prev:delafossite (cas 12013-12-6) CuFeO2 thin films via aerosol assisted CVD: Synthesis and characterization
Next:Three inter-linked active sites in the dehydrogenation of n-octane over MAGNESIUM MOLYBDATE (cas 12013-21-7) based catalysts and their influences on coking and cracking side reactions) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- delafossite (cas 12013-12-6) CuFeO2 thin films via aerosol assisted CVD: Synthesis and characterization08/01/2019
- Recovery of Ag and Au from synthetic and industrial wastewater by 2-step ferritization and Lt-delafossite (cas 12013-12-6) process via precipitation07/31/2019
- The influence of thermal properties of delafossite (cas 12013-12-6) nanofluid CuAlO2 on the turbulent natural convection inside a cavity07/30/2019
- Figure of merit improvement of delafossite (cas 12013-12-6) CuAlO2 with the addition of Fe and graphene07/29/2019
- Raman spectroscopy of (Fe,Li)-doped delafossite (cas 12013-12-6) oxide CuCrO207/28/2019
- Conductivity in (Ag,Mg)-doped delafossite (cas 12013-12-6) oxide CuCrO207/27/2019
- Fabrication and characteristic of delafossite (cas 12013-12-6)-type CuFeO2 nanofibers by electrospinning method07/26/2019
- Temperature dependent thermoelectric properties of cuprous delafossite (cas 12013-12-6) oxides07/25/2019
- Spin states investigation of delafossite (cas 12013-12-6) oxides by means of X-ray absorption and photoemission spectroscopy07/24/2019