Improved resistance of LANTHANUM ZIRCONATE (cas 12031-48-0) coatings to calcium-magnesium-alumina-silicate corrosion through composition tailoring

Add time:08/01/2019    Source:sciencedirect.com

Calcium–magnesium–alumina–silicate (CMAS) corrosion resistance is an important issue on the design of next-generation thermal battier coatings. As one of the promising thermal battier coatings, the LANTHANUM ZIRCONATE (cas 12031-48-0) coating has attracted continuous attention. In this work, three lanthanum zirconate coatings with different La/Zr composition, i.e., La1.8Zr2.2O7.1, La2Zr2O7, and La2.5Zr1.5O6.75, are fabricated by laser-enhanced chemical vapour deposition, and their resistance to CMAS corrosion at 1250 °C is investigated. Among them, La2.5Zr1.5O6.75 shows the best CMAS corrosion resistance because increased La content is beneficial to the formation of a dense and continuous apatite Ca2La8(SiO4)6O2 layer, which effectively slows down the subsequent molten CMAS penetration. This study clarifies the significant role of rare earth on CMAS corrosion resistance and is expected to guide the future design of rare-earth-based thermal battier coatings through composition tailoring.

We also recommend Trading Suppliers and Manufacturers of LANTHANUM ZIRCONATE (cas 12031-48-0). Pls Click Website Link as below: cas 12031-48-0 suppliers

Prev:LANTHANUM ZIRCONATE (cas 12031-48-0) ceramic toughened by ferroelastic domain switching of LaAlO3
Next:Exceptionally high fracture toughness of carbon nanotube reinforced plasma sprayed LANTHANUM ZIRCONATE (cas 12031-48-0) coatings)