Experimental investigation of Barium hydroxide octahydrate (cas 12230-71-6) as latent heat storage materials
-
Add time:08/06/2019 Source:sciencedirect.com
Phase change materials have a predominant role in heat storage technology. This paper focused on experimental study of Barium hydroxide octahydrate (cas 12230-71-6) (BHO-Ba(OH)2·8H2O), which is a low temperature phase change material with the melting point at 78 °C and a large latent heat with reported values in a range of 233 kJ/kg to 332 kJ/kg. Despite the great advantage of large heat capacity, it has significant supercooling and phase separation phenomena during the cooling process, which has limited its application. In this paper, five nucleating agents have been added to BHO to suppress the supercooling phenomena, including sodium borate, copper powder, calcium fluoride, calcium chloride and calgon. The experimental results indicated that the addition of 1% copper powder, 1% calcium fluoride, and 1% calgon by weight can reduce the supercooling degree to 2.7 °C, 1.8 °C and 2.3 °C respectively. In addition, gelatin has been used to suppress the phase separation phenomenon. The results indicate that the addition of 1% gelatin can hinder the phase separation by observing obvious less solid accumulations after 30 thermal cycles. Moreover, the thermal conductivity, specific heat capacity and corrosion characteristics were also measured in the experiments. The nucleating and gelling agents have successfully minimized the supercooling and phase separation issues of Ba(OH)2·8H2O, which is essential for its application as phase change material for thermal storage.
We also recommend Trading Suppliers and Manufacturers of Barium hydroxide octahydrate (cas 12230-71-6). Pls Click Website Link as below: cas 12230-71-6 suppliers
Prev:Superconductivity to 21 K in intermetallic thorium-based boride carbides
Next:Two-step process for production of methyl ester from rubber seed oil using Barium hydroxide octahydrate (cas 12230-71-6) catalyst: Process optimization) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Pyroelectric performances of 1-3 ferroelectric composites based on barium titanate nanowires/polyvinylidene fluoride08/15/2019
- Synthesis and crystal structure analysis of a novel microporous barium-containing silicate AES-2008/14/2019
- Preparation and properties of the barium borate glassy matrix composite materials containing fused silica and monoclinic zirconia08/13/2019
- Thermal decomposition of the hydrates of barium hydroxide08/12/2019
- Barium uranyl diphosphonates08/11/2019
- Green synthesis and characterization of 8-hydroxyquinoline barium (BaQ2)08/10/2019
- Setting process of lime-based conservation mortars with barium hydroxide08/09/2019
- Experimental Investigation of Improved Thermal Characteristics of Al2O3/Barium Hydroxide Octa Hydrate as Phase Change Materials (PCMs)08/08/2019
- Two-step process for production of methyl ester from rubber seed oil using Barium hydroxide octahydrate (cas 12230-71-6) catalyst: Process optimization08/07/2019
-
Health and Chemical more >