Effect of Triisopropanolamine (cas 122-20-3) on compressive strength and hydration of cement-fly ash paste
-
Add time:09/05/2019 Source:sciencedirect.com
This paper aims to investigate the effect of Triisopropanolamine (cas 122-20-3) (TIPA) on compressive strength and hydration of cement-fly ash paste. The samples with various dosages of TIPA were prepared with 30% fly ash (FA) and 70% cement (water/binder ratio by weight = 0.38), and cured under the standard condition. The compressive strength, pore structure, hydration process, and hydration products were investigated. The results show that TIPA can obviously increase the compressive strength of cement-FA system at the age of 7 d and 60 d, and the reasons are involved in pore structure and hydration of cement-FA system. Pore structure was characterized with mercury intrusion porosimetry, and the results show that TIPA can reduce total porosity but increase the amount of pore with size more than 50 nm, implying the air-entraining effect with negative effect on compressive strength. The result suggests that TIPA and defoaming agent should be used together to minimize the negative effect in real concrete. Furthermore, analysis of hydration products shows that TIPA can accelerate the hydration of both cement and FA, and this can also be illustrated from solid-state nuclear magnetic resonance. It is noticed that TIPA can hasten the conversion of AFt to AFm, which can be indicated from hydration heat. Additionally, the acceleration of pozzolanic reaction of FA is because TIPA can accelerate the dissolution of aluminate, silicate, and ferric into liquid paste which was demonstrated from morphology characterization and the change of ions in pore solution. Such results would be expected to provide experience for the use of alkanolamine in promoting the performance of cement-based materials.
We also recommend Trading Suppliers and Manufacturers of Triisopropanolamine (cas 122-20-3). Pls Click Website Link as below: cas 122-20-3 suppliers
Prev:Effect of Triisopropanolamine (cas 122-20-3) on compressive strength and hydration of steaming-cured cement-fly ash paste
Next:Sulfate adjustment for cement with Triisopropanolamine (cas 122-20-3): Mechanism of early strength enhancement) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Formation and structure of tris(alumatranyloxy-i-propyl)amine directly from Al(OH)3 and Triisopropanolamine (cas 122-20-3)09/25/2019
- On the mechanism of strength enhancement of cement paste and mortar with Triisopropanolamine (cas 122-20-3)09/24/2019
- Solubilities of carbon dioxide in aqueous solutions of Triisopropanolamine (cas 122-20-3)09/10/2019
- Interaction effect of Triisopropanolamine (cas 122-20-3) and glucose on the hydration of Portland cement09/09/2019
- In situ nano-Fe3O4/Triisopropanolamine (cas 122-20-3) functionalized graphene oxide composites to enhance Pb2+ ions removal09/08/2019
- Hydration of ternary cement in the presence of Triisopropanolamine (cas 122-20-3)09/07/2019
- Sulfate adjustment for cement with Triisopropanolamine (cas 122-20-3): Mechanism of early strength enhancement09/06/2019
- Effect of Triisopropanolamine (cas 122-20-3) on compressive strength and hydration of steaming-cured cement-fly ash paste09/04/2019
-
Health and Chemical more >
-
Related Products