Synthesis and characterization of nickel cobalt zinc ferrous hydrazine fumarate

Add time:09/30/2019    Source:infona.pl

Hydrazinated nickel cobalt zinc ferrous fumarate precursor has been synthesized and decomposed autocatalytically to Ni0.4Co0.2Zn0.4Fe2O4. The thermal decomposition behavior of the precursor has been investigated by thermogravimetric (TG) and differential thermal analysis (DTA). The chemical composition was assigned to precursor based on chemical analysis, TG–DTA, infrared (IR), isothermal mass loss, and total mass loss studies. The X-ray powder diffraction of the decomposed precursor confirms the formation of monophasic nickel cobalt zinc ferrite, and IR spectrum exhibits two peaks in the region of 340–420 and 550–660 cm−1 characteristic of spinel ferrites. The average grain size evaluated by TEM is found to be 15–20 nm. The electrical DC resistivity measurement was carried out with respect to temperature using two-probe method and dielectric properties as a function of frequency. The high dielectric constant values found at lower frequencies were due to nanosize nature of the “as prepared” ferrite. The Curie temperature of the “as-prepared” Ni0.4Co0.2Zn0.4Fe2O4 determined by alternating current susceptibility measurements was found to be 380 °C.

We also recommend Trading Suppliers and Manufacturers of Ferrous fumarate (cas 141-01-5). Pls Click Website Link as below: cas 141-01-5 suppliers

Prev:Microencapsulation for iodine stability in salt fortified with Ferrous fumarate (cas 141-01-5) and potassium iodide
Next:The development of electrically conductive polycaprolactone fumarate–polypyrrole composite materials for nerve regeneration)