Ordered CeO2 nanotubes (CeO2-T) were prepared via a hydrothermal synthesis process using the triblock copolymer polyethylene oxide-polypropylene oxide-polyethylene oxide (P123) as a morphology control agent. CeO2-T characterization demonstrated the formation of single crystal structures having lengths between 1-3 μm and diameters < 100 nm. A supported Pd catalyst (Pd/CeO2-T) was also prepared through hydrothermal means. H2-temperature reduction profile and Raman spectroscopy analyses showed that the oxygen vacancies on the CeO2 surface increased and the reduction temperature of the surface oxygen decreased after Pd loading onto CeO2-T. Pd/CeO2-T was employed as a catalyst toward the oxidative carbonylation of phenol and the reaction conditions were optimized. Phenol conversion was 53.2% with 96.7% selectivity to diphenyl carbonate under optimal conditions. The integrity of the tubular CeO2 structure was maintained after the catalyst was recycled, however, both activity and selectivity significantly decreased, which was mainly attributed to the Pd active component significantly leaching during the reaction.
View Morewebsite:http://www.shtopchem.com/
Contact:0086-0576-87776998
Address:room no 1608,xuhui business building yude road,xujiahui street, xuhui district
Contact:021-36356756
Address:Room601,Building No.14,280 Yangcheng Road,Shanghai
Beijing Apis Biotechnology Co., Ltd.
Contact:86-010-67856775-8551
Address:NO.4PUHUANGYU ROAD,FENTAI DISTRICT, BEIJING, CHINA
Hangzhou JINLAN Pharm-Drugs Technology Co., Ltd
website:http://www.jlpharms.com
Contact:+86-571-86982636
Address:Rm A606, Fuyi Center, jianqiao street, Jianggan Area
Contact:(86) 731 88718666
Address:Room 1222, Unit 4, Building B, Shangcheng, No.47, Kaiyuan East Road.
Doi:10.1080/00958972.2010.508284
(2010)Doi:10.1691/ph.2010.9345
(2010)Doi:10.1021/acs.biochem.0c00831
(2020)Doi:10.1016/j.molstruc.2020.127916
(2020)Doi:10.1002/adsc.201300255
(2013)Doi:10.1021/jo016078v
(2001)